Abstract The dechlorination efficiency of zinc oxide dust using microwave roasting was investigated capitalizing on the different microwave absorbing capacities of the compounds such as chlorine, lead, and zinc oxide. The associated dechlorination reactions were discussed in detail and the effect of all the influencing parameters such as the air flow rate, steam flow rate, the roasting temperature, roasting duration, and the mixing rate were assessed to identify the optimal conditions. The results indicated that a near 93% dechlorination of zinc oxide dust could be achieved, which would satisfy the requirements of the wet smelting electrolysis process. The optimal process parameters were identified to be an air flow of 300 L/h, a steam flow of 8 mL/min, a stirring speed of 60 rpm, a roasting temperature of 650 ºC, and a roasting duration of 60 min. Water vapor has an enhanced effect on dechlorination by microwave roasting.

Abstract In this research, the effect of different citric acid concentrations, ammonia concentration, temperature, leaching time, stirring speed and liquid-to-solid ratio on the zinc leaching from low-grade zinc oxide ore in a NH3-H3C6H5O7-H2O system were studied. The results showed that the zinc leaching rate is only 4.7% when the citric acid concentration is 0 M, and the leaching efficiency of Zn increased with increasing citric acid concentration. Under the conditions: citric acid concentration of 1.0 M, ammonia concentration of 6 M, temperature of 25 °C, leaching time of 60 min, stirring speed of 300 rpm and the starting solid-to-liquid ratio of 1:5, 81.2% of Zn is leached. The mineralogical changes of the low-grade zinc oxide ores during the processes were characterized by X-ray fluorescence (XRF), X-ray powder diffraction (XRD), Scanning Electron Microscopy associated with Energy Dispersive Spectroscopy (SEM-EDS) and Fourier transform infrared spectroscopy (FT-IR). From the evidence we deduced that citric ions complexed with zinc ions, forming a Zn-citrate complex. As a result, the zinc leaching rate was improved without the risk of pollution or pretreatment. This makes it as a good choice for a more ecological treatment of hemimorphite.